Bronze Flange, Bronze Plate, Aluminum Bronze Plate, C95400 Plate

• Type: Plate
• Material: Bronze
• Shape: Square
• Alloy: Alloy
• Color: Golden
• Standard: ASTM
• Model NO.: Aluminum Bronze plate
• Aluminum Bronze Plate: C95400 Plate
• Transport Package: Plywood Box/Wooden Box/Pallet
• Specification: ASME/ANSI/DIN/BS/JIS
• Trademark: C&N
• Origin: China
• Production Capacity: 600tons. /Month

Product Description

Aluminum bronze is the highest strength standard copper based alloy. Concast produces C95400, C95500 and C95900 in standard sizes of rounds, tubes and rectangles. Aluminum in conjunction with iron and nickel in C95500 acts as a strengthener in these alloys. All of the aluminum bronzes can be heat treated, further increasing tensile strengths.



Product Description: Aluminum Bronze
Solids: 1/2" to 9" OD
Tubes: 1 1/8" to 9" OD
Rectangles: Up to 15"
Standard Lengths: 144"
Shape/Form: semi-finished, mill stock or near-net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or structural shape, flats/rectangular bar
Compliance: C95400 is compliant with key legislation including (1) Federal Safe Drinking Water Act 1974 - SDWA, (2) Federal Reduction of Lead in Drinking Water Act 2011 and (3) California AF1953
Typical Uses
Automotive weld guns
Fasteners nuts, large hold down screws
Industrial bushings, high strength clamps, gears, valves, bearings, pawl, valve bodies, landing gear parts, worm gears, machine parts, pressure blocks for the steel industry, bearing segments for the steel industry, valve seats, valve guides, pickling hooks, spur gears, heavily loaded worm gears, pump parts
Marine covers for marine hardware, ship building
Ordnance government fittings
 
Note: Also available in a heat-treated condition.
 
Similar or Equivalent Specification

CDA	ASTM	ASARCON	SAE	AMS	Federal	Military	Other
C95400	B505				QQ-C-390, G5; QQ-B-671, CLASS 3	MIL-B-16033, CLASS 3	ALUMINUM BRONZE 9C

Chemical Composition (according to ASTM B505/B505M-14)

Alloy	Cu%	Fe%	Ni%1	Al%	Mn%
1Ni value includes Co. Note: Cu + Sum of Named Elements, 99.5% min. Single values, unless otherwise noted, represent maximums.
C95400	83.00	3.00- 5.00	1.50	10.0- 11.50	0.50

Mechanical Properties (according to ASTM B505/B505M-14)

Tensile Strength(min)	Yield Strength(at .5% extention under load min)	Elongation(in 2in. or 50mm min, %)	Brinell Hardness(typical Bhn - 3000kg)	Remarks
Ksi	MPa	Ksi	MPa
85		32		12	170

Machinability

Alloy	Rating	Density
C95400	60	0.269

Physical Properties (provided by CDA)

	US Customary	Metric
* TQ 50 Temper, Field Strength 16 kA/m ** As Cast, Field Strength 16 kA/m
Melting Point - Liquidus	1900° F	1038° C
Melting Point - Solidus	1880° F	1027° C
Density	0.269 lb/in3 at 68° F	7.45 gm/cm3 at 20° C
Specific Gravity	7.45	7.45
Electrical Resistivity	80.20 ohms-cmil/ft at 68° F	13.33 microhm-cm at 20° C
Electrical Conductivity	13% IACS	0.075 MegaSiemens/cm at 20° C
Thermal Conductivity	33.90 Btu · ft/(hr · ft2 · °F) at 68° F	58.7 W/m at 20° C
Coefficient of Thermal Expansion	9 · 10-6 per °F (68°-572° F)	16.2 · 10-6 per °C (20°-300° C)
Specific Heat Capacity	0.10 Btu/lb/°F at 68° F	419.0 J/kg at 293° C
Modulas of Elasticity in Tension	15500 ksi	107000 MPa
Magnetic Permeability*	1.20	1.20
Magnetic Permeability**	1.27	1.27